fuchs

The Plug is back - V2 HotEnd :-( How to clean?

Recommended Posts

Today i got new, black Filament from fabberworld.com. Very nice, not translucent, deep black.

So I decided to give it a go and printed same parts of the InMoov Hand (http://www.thingiverse.com/thing:17773). I printed them at 220 degrees, 2mm retraction. No Problems.

Then I decided to test the retraction capabilities and temperature characteristics of the Filament and printed (several times) the hollow calibration pyramid (http://www.thingiverse.com/thing:21303).

First at 220 degrees, 2mm retraction (80mm/s speed). After that I tried 220 degrees and 4mm retraction. Went both kinda well (but not perfect). Then I tried 215 degrees, 4mm retraction and ran into problems, as the filament didn't look right anymore. Raised temperature to 220 (while printing) and that improved the situation a bit.

But at that time I noticed that some black PLA tried to leak out between the PEEK and the brass - it made a black shadow at the junction, but didn't flow out.

So tried to print the pyramid again at 230 degrees, 4mm retraction but after the basic layer, there was a lack of filament. I removed the filament and *tadaaa* pulled out a plug.

What the?

How to clean the Hotend now? Disassemble while hot and then what?

I understand that a too low temperature will form a plug as the filament doesn't get liquefied and pressure builds up (as in my case). But how to get rid of that plug for good? And what steps need to be taken to clean the Hotend???

HELP, plz! :(

Share this post


Link to post
Share on other sites

I can't help you on the plug but I just cleaned the PLA off from my parts because of a leak. What I did was I seperated the parts from the heater block and heated the brass parts with a flame until the plastic liquefied and wiped it off with a cloth. I repeated the steps until they were clear, just make sure you free up the threads. I also took a flame to it before I connected the brass parts again to get rid of any fibers from the cloth.

Not sure how good this advice is since I haven't pieced mine back together 100% yet but the parts that did go back on, went without issue. Good luck!

Share this post


Link to post
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now
Sign in to follow this  

  • Our picks

    • Introducing Ultimaker Cura 3.6 | Beta
      Ultimaker Cura 3.6 | Beta is available. It comes with new features, bug fixes, and UX improvements. We would really like to have your feedback on it to make our stable release as good as it can be. As always, you can download the beta for free from our website, for Windows, MacOS, and Linux.
        • Like
      • 75 replies
    • Print Core CC | Red for Ruby
      Q: For some users, abrasive materials may be a new subject matter. Can you explain what it is that makes a material abrasive when you are not sure which print core to use?
      A: Materials which are hard in a solid piece (like metals, ceramics and carbon fibers) will generally also wear down the nozzle. In general one should assume...
        • Like
      • 24 replies
    • "Back To The Future" using Generative Design & Investment Casting
      Designing for light-weight parts is becoming more important, and I’m a firm believer in the need to produce lighter weight, less over-engineered parts for the future. This is for sustainability reasons because we need to be using less raw materials and, in things like transportation, it impacts the energy usage of the product during it’s service life.
        • Like
      • 12 replies
×

Important Information

Welcome to the Ultimaker Community of 3D printing experts. Visit the following links to read more about our Terms of Use or our Privacy Policy. Thank you!