Posted · NinjaFlex Profile on UM2+

I have been using NinjaFlex for the past few weeks and have been fidgeting with the settings and found some pretty decent ones. I have not been able to find good profile recommendations so please post what you are using to compare. I am using a stock UM2+ with a universal filament filter to keep the NinjaFlex oiled as it enters the tube. Retraction settings turned off. UM2+ completely enclosed. Blue Painters Tape to ensure plate adhesion.

Cura 2.5.0:

Nozzle: 0.4mm

Layer Height: 0.2mm

Initial Layer Height: 0.3mm

Wall Thickness: 0.8mm

Top/Bottom Thickness: 0.8mm

Print Speed: 30mm/s

Infill Speed: 30mm/s

Top/Bottom Speed: 30mm/s

Travel Speed: 115mm/s

Initial Layer Speed: 30mm/s

Fan Speed: 60%

Regular Fan Speed: 35%

Initial Fan Speed: 0%

Ultimaker 2+:

Temperature: 240C

BuildPlate Temp: 45C

Material Flow: 110%

  • Share this post

    Link to post
    Share on other sites
    • 8 months later...
    Posted · NinjaFlex Profile on UM2+

    Hi future readers,

    Good settings. Used them to refresh my memory after a year of not printing NinjaFlex.
    Another tip:

    ** Buy Yourself A PTFE Bowden Tube **

    On my UM2+ I have printed NinjaFlex with mixed results a year ago.
    Last week I used it again for a new project and had difficulties finding the right settings. Adding 5-10% flow is essential but also on high temp and freshly cleaning (atomic pull) nozzle worked well 1 print, failed the next one etc. Under extrusion from the start or suddenly after quite some layers. With the clean nozzle the only problem could be the feeding. Cleaning the feeder and fresh undented NinjaFlex filament didnt fix it.

    So I expected the flex filament being spaghetti in the non-PTFE Ultimaker bowden tube would cause too much friction at those under-extrusion moment. And indeed, sometimes the filament looked to be pushed fairly straight, but often when under good pressure it curled in S-shape/zig-zag like way as the UM bowden inside dimater is larger than the 2.85-3mm filaments.

    I read good stories about the lower friction of PTFE tubes. Bought one (from the RepRap guys here in The Netherlands) and after install print was just fine. You also really feel the different in friction when you compare by feeding filaments through both.
    The one I bought from RepRap also has a smaller inside diameter I noticed, leaving less room for heavy zig-zag'ing which I think causes the heaviest friction.

    Buy yourself one if you have trouble. You need 73cm, they often are sold per 10cm.
    Only downside, they are not fully transparent. Translucent to almost solid white. If you really like to see your filament moving or spot dirt in your tube this might be a disadvantage. If not, nothing to loose here.

    Good luck guys

  • Share this post

    Link to post
    Share on other sites

    Create an account or sign in to comment

    You need to be a member in order to leave a comment

    Create an account

    Sign up for a new account in our community. It's easy!

    Register a new account

    Sign in

    Already have an account? Sign in here.

    Sign In Now
    • Our picks

      • Talking additive | The 3D printing podcast
        Why should we be the only ones asking questions? Join us and ask Jabil all your questions on September 22nd 5pm CET
          • Like
        • 3 replies
      • Ultimaker masterclass: Optimizing your Ultimaker Cura workflow
        Save your seat for either broadcast on September 23.
        What will you learn?
        · Best practices for iterative print preparation and every lesson you should learn from each print
        · The right way to use per-object settings and when they are most useful
        · Easy-to-use resources for anyone who wants to develop their own printer definitions, plugins, or print profiles
        · How to optimize print profile settings and whether to “keep” or “discard” changes
        · When is the right time to export your drawing from CAD? (Based on Ultimaker Cura’s surprising power as 3D control software)
        · And a whole lot more tips and tricks!
        How can I join?
        This free masterclass will take place twice:
        1. 11am CEST (5pm SGT, 5am EDT)
        2. 5pm CEST (11am EDT, 8am PDT, 11pm SGT)
          • Like
        • 0 replies
      • Do you use 3D printing at work? Let us know
        It doesn't matter if you are using 1 Ultimaker or 10, there is inspiration in everything. We're looking for ...
        • 1 reply
    • Create New...