XT-CF20 settings help...

Recommended Posts

Posted · XT-CF20 settings help...

Hi,

 

I have a UM2+ with a Bondtech extruder (recently fitted) and a ruby nozzle.

I have been experimenting with ColorFabb XT-CF20 over the past few days. I have been struggling with getting my settings spot on...

I first used the average settings suggested by colorfabb (250degC, 65degC bed, 50% fan, 55mm/s print speed, plus other standard settings).

My first print created lots of stringing, so I designed a basic part to test for stringing and tried again...

 

Capture.thumb.JPG.7ffa00b567ea042d4da2075af10964e5.JPG20190610_143449.thumb.jpg.2ce6ace71aa0c25d60cd79b9ca20442c.jpg

 

To counteract this I tried reducing the temp to 240degC and increasing retraction length to 10mm. This definitely helped, but it still isn't perfect (especially at the top of the prints).

 

I have tried a number of prints varying print temp and retraction length to try and reduce the stringing. I still can't get a perfect result.

My second print is the best one, but there is still a very small string at the top of the print and looks like it might be starting to under extrude.

 

IMG_20190612_144814.thumb.jpg.3c0494db6215d6e73531e3506ef52d05.jpg

 

I am going to set off another print, but at a slower speed to see if that helps. Does anybody else have any further suggestions?

 

TIA,

Rich

 

P.S. The nozzle also gets caked very easily. Any ideas? (hoping this is unrelated)

 

 

20190610_143449.jpg

IMG_20190612_144814.jpg

Share this post


Link to post
Share on other sites
Posted (edited) · XT-CF20 settings help...

HiHi,
i have opened a french discussion with my parameters here : 

 

Here's my parameters :

- UMO+ V2 ( means it has the same motherboard as you)

- E3DV6 + hardened steel nozle

 

=> custom firmware to reach 280°C

=> PID autotune done at 280°C

=> extruder calibration done

 

cube single shell and temperature Tower printed

results :

 

- flow rate 80%

- 280°C printing

- retractation 6.5mm

- print speed 20mm/min (need to be tested at 40mm/min to reduce print time)

- layer height 0.2mm

 

There are photos of my temp tower in the other post

Edited by Catlord

Share this post


Link to post
Share on other sites
Posted · XT-CF20 settings help...

Hi @rich080487,

those aren’t strings, they are “antennae”.  Whereas strings are material sticking to the just-printed object as the head travels to the next, these are formed as the head completes travel to the new part. A small drop is hanging from the nozzle and attaches to the outside of the prior layer. Next layer, the drop hits that previous drop, and so on. This is why they grow up and away from the part.

 

Temperature doesn’t affect these much. I think retraction may be the thing to focus on.

Share this post


Link to post
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now

  • Our picks

    • Survey: Understanding your workflow
      Interact with future concepts and aim to collect your feedback and opinion. In particular, if this would/could be a welcome addition to your 3D printing workflow. Interested?
      • 0 replies
    • Coronavirus: Let's do our part
      Through this post I would like to further explain what we are doing, and what you could be doing. 
      Our efforts consist of 2 layers. First; connect medical institutions and hospitals to (local) 3D Printing hubs to help them print parts of which a 3D model already exists. And second, contribute to design the necessary part and then have it printed via a (local) 3D printing hub. Experts are available from within Ultimaker and from within our network of 3D printing experts.
        • Like
      • 53 replies
×
×
  • Create New...

Important Information

Welcome to the Ultimaker Community of 3D printing experts. Visit the following links to read more about our Terms of Use or our Privacy Policy. Thank you!