Posted · drop formation at UM3

Hi, 

 

I have got problems with my Ultimaker 3. 

When I print thin things like cookie cutters, it is not smooth. There are little points and also very little wholes in the object. Only thin prints up to about 1 cm are affected. On bigger things is everything ok. I have read for hours and I tried to solve the problem.

The Material is PLA. 

I tried different temperatures and infills, because I often read that I should reduce the temperature(but that doesn't help). 

All other settings were from the standard profile of Ultimaker PLA. 

 

Can you help me with that problem?

 

Thank you in advance

Best regards

Raphael Ostheimer 

20200816_160220.jpg

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    I'm not sure if you have A) bad slicing or B) underextrusion

     

    A) 

    Can you show what this looks like in layer view please?  Are there "holes" in the same spots as where you actual print showed holes?

     

    Maybe try checking the box "print thin walls".  Also maybe try burtoogle version of slicer which deals with thin walls nicely.

     

    B) It could be ordinary underextrusion.  If so try printing at 1/3 the speed just to see if that makes a difference.  Also make *all* the printing speeds the same speed.  There are many causes of underextrusion (dozens) but they are all improved by printing at 1/3 speed.  You can do this from the TUNE menu on most printers including the UM3.

     

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    Hi gr5,

     

    thank you for your reply.

     

    I had activated "print thin walls". 

    The wholes weren't shown in the slicer. In Cura it looks perfect. 

     

    Now, it is printing it with 20 mm/s. I can say if it helped when the print has finished. 

    I am printing with the AA04 Print Core, but I also have the AA0.25 or the AA08 available. 

     

    I noticed that the problem is only when the wall is smaller than the housing. 

     

    I'll be in touch,

    Once again many thanks,

    Raphael

    hilfe ultimaker.JPG

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    Hi gr5,

     

    thank you for your reply.

     

    I found out that the profile of the infill has allways the same problem. Could that be underextrusion?

     

    I had activated "print thin walls". 

    The wholes weren't shown in the slicer. In Cura it looks perfect. 

     

    Now, it is printing it with 20 mm/s. I can say if it helped when the print has finished. 

    I am printing with the AA04 Print Core, but I also have the AA0.25 or the AA08 available. 

     

    I noticed that the problem is only when the wall is smaller than the housing. 

     

    I'll be in touch,

    Once again many thanks,

    Raphael

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    Did you check *all* the speeds in Cura?  There are 7 printing speeds I think.  Did you check all 7?

     

    Usually infill is printed at double speed.

     

    20mm/sec doesn't mean much.  The *volume* is more important.  The feeder is only strong enough to push at a certain volume.  So for example 0.4 line width with 40mm/sec with 1mm layers (crazy thick layers!!) would be 40*0.4*1 = 16mm^3/sec.  That's on the edge of what a UM3 can do.  But if your layer height is 0.2, speed is 40, and line width is 0.4 then that's 1/5 the volume (thinner layers) and only 3.2^3mm/sec.  Very easy to do.  If you are still getting underextrusion at a volume of 3.2 then something is seriously wrong.  But what was the infill speed?  What was the layer height.

     

    Anyway, if the slower speed helps and if you had layers around 0.1 or 0.2 thick then you have a mechanical problem.  Try doing some cold pulls.  It's in the UM3 menu system.  I think under maintenance maybe?

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    That is imortant, I will note it down. 

    The layer high was 0.1mm. 

    The print with 20mm/s is much better than them before. 

    -> so it is 0,8mm3/s

    There is still a bit of underextrusion, could it help to clean the printcore?

    I made a screenshot from the speed settings, which I took for the print. The infill was not the right speed. 

     

     

    20200817_113759.jpg

    hilfe ultimaker2.JPG

  • Link to post
    Share on other sites

    Posted · drop formation at UM3

    So your printer should be able to print about 8X that volume per second.  So something is seriously wrong.  I'll give you a list of possibilities.  I'd concentrate on cleaning the core.  Quick diagnostic is to pop in the other AA 0.4 core and see if it's all better.

     

     

    CAUSES FOR UNDEREXTRUSION ON UM3 AND HOW TO TEST FOR THEM AND REMEDY THEM

    As far as underextrusion causes - there's just so damn many.  none of the issues seem to cause more than 20% of problems so you need to know the top 5 issues to cover 75% of the possibilities and 1/4 people still won't have the right issue.  Some of the top issues:
    1) Print slower and hotter!  Here are top recommended speeds for .2mm layers (twice as fast for .1mm layers) and .4mm nozzle:
    20mm/sec at 200C
    30mm/sec at 210C
    40mm/sec at 225C
    50mm/sec at 240C
    The printer can do double these speeds but with huge difficulty and usually with a loss in part quality due to underextrusion.  Different colors print best at quite different temperatures and due to imperfect temp sensors, some printers print 10C cool so use these values as an initial starting guideline and if you are still underextruding try raising the temp.  But don't go over 240C with PLA.

    Note that your "print speed" may be 40mm/sec but it may be printing infill at 80mm/sec so CHECK ALL SPEEDS.

    2) Line Width larger than nozzle.  In cura 3.X search in settings for all line widths.  If any of them are larger than the nozzle diameter this can cause underextrusion.  There are 8 of these in cura 3.2.1.

    3) Curved filament at end of spool - if you are past half way on spool, try a fresh spool as a test.

    4) curved angle feeding into feeder - put the filament on the floor -makes a MASSIVE difference.

    5) Bad core.  Try a different core.  It could be clogged, or something more complex like the temp sensor in the core.

    5a) clogged nozzle - the number one most suspected problem of course.  Sometimes a grain of sand gets in there but that's more obvious (it just won't print).  Atomic method (cold pull) is the cure - from the menu do a few cold pulls.  The result should be filament that is the exact shape of the interior of the nozzle including the tiny passage to the tip of the nozzle.  If it doesn't look like that you need to pull at a colder temperature.  You can do it manually instead of through the menu if it's not working right but learn through the menu initially.  95C is roughly the correct "cold" temperature for PLA.  Higher temps for other filaments. Simpler cold pull (3dsolex cores only - doesn't work on ultimaker cores because you can't remove the nozzle): https://www.youtube.com/watch?v=u07m3HTNyEg


    5b) Temp Sensor bad - even the good ones vary by +/- 5C and bad ones can be any amount off - they usually read high and a working sensor can (rarely) fail high slowly over time.  Meaning the sensor thinks you are at 220C but actually you are at 170C.  At 170C the plastic is so viscous it can barely get out of the nozzle.  You can verify your temp sensor using this simple video at youtube - on you tube search for this: mrZbX-SfftU


    6) feeder spring issues - too tight, too loose.  You want the tension such that you can clearly see the diamond pattern biting into the filament.  You want to see at least 2 columns of diamonds.  4 columns is too much.  You usually want the tension in the center.  If the white marker isn't in the center, make sure the adjustment screw actually moves the marker.  If not then someone put the feeder back together wrong.

    7) Other feeder issues, one of the nuts holding UM2 and UM3 together often interferes with the feeder motor tilting it enough so that it still works but not very well.  Other things that tilt the feeder motor, sleeve misaligned so it doesn't get a good grip.  Gunk clogging the mechanism in there.

    😎 Filament diameter too big - 3mm is too much.  3mm filament is usually 2.85mm nominal or sometimes 2.9mm +/- .05.  But some manufacturers (especially in china) make true 3.0mm filament with a tolerance of .1mm which is useless in an Ultimaker.  It will print for a few meters and then clog so tight in the bowden you will have to remove the bowden from both ends to get the filament out.  Throw that filament in the trash!  It will save you weeks of pain

    8b) Something wedged in with the filament.  I was setting up 5 printers at once and ran filament change on all of them.  One was slowly moving the filament through the tube and was almost to the head when I pushed the button and it sped up and ground the filament badly.  I didn't think it was a problem and went ahead and printed something but there was a ground up spot followed by a flap of filament that  got jammed in the bowden tube.  Having the wedgebot (link below) helps you feel this with your hand by sliding the filament through the bowden a bit to see if it is stuck.

    https://www.youmagine.com/designs/wedgebot-for-ultimaker2

    9) Extruder mis calibrated.  Maybe you changed equipment or a wire fell off.  Try commanding the filament to move exactly 100mm and then measureing with a ruler that it moved 100mm within 10% accuracy.  If not adjust the steps/mm (this is done by editing a json file on the UM3).

    10) Z axis steps/mm.  it's easier than you might think to double or half the Z axis movement as there is a jumper on the circuit board that can be added or removed.  If the Z axis is moving 2X you will get 50% underextrusion.  Your parts will also be 2X as tall.

    11) Crimped bowden.  At least one person had an issue where the bowden was crimped a bit too much at the feeder end although the printer worked fine when new it eventually got worse and had underextrusion on random layers.  it's easy to pull the bowden out of the feeder end and examine it.  Similar to 8b above - use the wedgebot to feel how much friction there is in the bowden.

    12) Worn Bowden.  After a lot of printing (or a little printing with abrasive filaments) the bowden resistance can be significant. It's easy to test by removing it completely from the machine and inserting some filament through it while one person holds it in the U shape.  Preferably insert filament that has the pattern from the feeder and fight the movement by applying 2kg force on both ends at the same time and then seeing how much harder you have to push it on top of 1kg force.  UM2 feeders can push with 5kg force.  UM3 can push quite a bit more.  5kg is plenty.

    13) Small nozzle.  Rumor has it some of the .4mm nozzles are closer to .35mm.  Not sure if this is actually true.  I'm a bit skeptical but try a .6mm nozzle maybe.  This shouldn't be a problem on the UM3 which has very good quality control but try a different core.

    14) CF filament.  The knurled sleeve in the extruder can get ground down smooth - particularly from carbon fill.  4 spools of CF will destroy not just nozzles but the knurled sleeve also.  Look at it visually where the filament touches the "pyramids".  Make sure the pyramids are sharp.

    15) Hot feeder driver.  I've seen a more recent problem in the forums (>=2015) where people's stepper drivers get too hot - this is mostly a problem with the Z axis but also with the feeder.  The high temps means the driver appears to shut down for a well under a second - there is a temp sensor built into the driver chip.  The solution from Ultimaker for the um2 is that they lowered all the currents to their stepper drivers in the newer firmware.  Another solution is to remove the cover and use desk fan to get a tiny bit of air movement under there.  This doesn't seem to be a problem on UM3 even though it's the exact same circuitry but they lowered the current in the firmware.  But it's worth considering if air temp is 30C or hotter.  It would probably happen only after printing for a while (air heats up slowly under the printer).


    16) third fan broken.  This tends to cause complete non-extrusion part way through a print.  In the door of the head.  You can hear it come on when cores get above 40C.  Without this fan several things can go wrong.  It can take a while as usually you also need several retractions to carry the heat upwards.  There are a few failure mechanisms and I don't understand them all.  One of them is probably that the molten PLA spreads out above the teflon and sticks to the metal in a core or fills the gap at the base of the bowden in UM2.  Later it cools enough to keep the filament from moving up or down.

    17) Spiralize/vase mode.  This is a rarely used feature of Cura but you might have left it on by accident?  In this mode the wall of your part is printed in a single pass.  So if you have a .4mm core and the wall is .8mm thick it will try to over extrude by 2X.  This is difficult to do and may instead lead to underextrusion.

    18) too many retractions (this causes complete failure) - if you have too many retractions on the same piece of filament you can grind it to dust.  10 is usually safe.  20 is in the danger zone.  50 should guarantee failure.  You can tell cura to limit retractions to 10 per a given spot of filament.  Do this by setting "maximum retration count" to 10 and "minimum extrusion distance" to your retraction distance (4.5mm for UM2 and 6.5 for UM3).

    19) Brittle filament.  Espciallty with older PLA but even brand new pla can do this.  If you unspool some (for example if it's in the bowden) for many hours (e.g. 10 hours) it can get extremely brittle and it can snap off into multiple pieces in the bowden.  It's not obvious if you don't look for this.  Then it starts printing just fine and at some point one of those pieces reaches the print head and gets hung up somewhere and the printer suddenly stops extruding for now apparent reason.  This usually happens within the first meter of filament - once you get to printing the filament that was recently on the spool it should be fine from then on.

    20) The "plus" feeder can have an issue where the filament doesn't sit properly for one print and it permanently damages the arm inside the feeder as shown by this photo - the hole is ground down asymetrically: http://gr5.org/plus_feeder_issue.jpg

    21) Filament tangle - the end of the filament can get tucked under a loop on the spool and this tangle can propagate from then forever to the end of the spool until you fix it.  It will cause many many jam ups and slow then halt extrusion.  Repeatedly.  The fix is to remove the filament from the printer, unroll a few meters and respool and put back on the printer.  Never let go of the end of the filament spool until it's in the bowden.
    =======
     

     

    • Like 2
    Link to post
    Share on other sites

    Posted · drop formation at UM3

    Sorry for my late answer, I was in vacation. 

    I cleaned the nozzle with hot and cold pulls and I tried to change the Filament. The results are much better than before. 

    I will try all tips you gave me, thank you so much. 

  • Link to post
    Share on other sites

    Create an account or sign in to comment

    You need to be a member in order to leave a comment

    Create an account

    Sign up for a new account in our community. It's easy!

    Register a new account

    Sign in

    Already have an account? Sign in here.

    Sign In Now
    • Our picks

      • Introducing Universal Cura Projects in the UltiMaker Cura 5.7 beta
        Strap in for the first Cura release of 2024! This 5.7 beta release brings new material profiles as well as cloud printing for Method series printers, and introduces a powerful new way of sharing print settings using printer-agnostic project files! Also, if you want to download the cute dinosaur card holder featured below, it was specially designed for this release and can be found on Thingiverse! 
          • Like
        • 10 replies
      • S-Line Firmware 8.3.0 was released Nov. 20th on the "Latest" firmware branch.
        (Sorry, was out of office when this released)

        This update is for...
        All UltiMaker S series  
        New features
         
        Temperature status. During print preparation, the temperatures of the print cores and build plate will be shown on the display. This gives a better indication of the progress and remaining wait time. Save log files in paused state. It is now possible to save the printer's log files to USB if the currently active print job is paused. Previously, the Dump logs to USB option was only enabled if the printer was in idle state. Confirm print removal via Digital Factory. If the printer is connected to the Digital Factory, it is now possible to confirm the removal of a previous print job via the Digital Factory interface. This is useful in situations where the build plate is clear, but the operator forgot to select Confirm removal on the printer’s display. Visit this page for more information about this feature.