Hi

Could you please give me your best advices for removing stringing?

I've followed the troubleshooting guide, hence tried different lower temperatures (all the way down to 180) at different lower speeds.

I've tried various combinations of retraction speed and retraction length, multiple filaments, but I just haven't been able to get a print without stringing from each retraction point to the next starting point.

Printing PLA on a UM2

Edited:

I get a combination of dots somewhere and lines elsewhere.

Thanks!

Kind regards Taras

 

Share this post


Link to post
Share on other sites

Did you run into underextrusion when lowering temperature? If not, try going further down. If you can go down further, then something is wrong with the temperature sensor.

Some filament has a tremendous tendency for stringing. Are you printing with pure PLA or with a PLA/PHA mixture?

 

Share this post


Link to post
Share on other sites

Another thought just crossed my mind: Make sure the nozzle is clean on the outside. If it gets covered by PLA, this has a adhesive effect onto further PLA and you get much more stringing. Maybe you have the situation that at some places material is not cooled down enough before the next layer is applied. This then leads to diving of the nozzle into the still soft PLA and getting covered.

 

Share this post


Link to post
Share on other sites

Didier > I'll try to increase travel speed to se if it "breaks" of the filement at retraction.

Dim3nsioneer > Hmm yes it is a bit 'dirty' from some of the ABS test I did. I'll try to clean it off.

Thanks - the both of you!

 

Share this post


Link to post
Share on other sites

1) Are you certain retraction is happening at all? There are 6 or so settings that control it. You can verify it in layer view.

2) Please post a picture because what you call stringing we might call something totally different like "bad Z axis" or underextrusion.

3) Consider increasing retraction distance. When my UM2 was new 5.5mm was perfect. Now that I have the bowden tube locked tight in the print head and it never moves up and down anymore I can do 4.5mm and that's perfect.

4) Some brands of PLA do a small amount of thin stringing no matter what you do.

5) Printing very slow (e.g. 20mm/sec) greatly reduces pressure in print head and reduces stringing to pretty much zero. But you shouldn't have to go this low. I recommend printing some kind of stringing test part like the first photo here:

http://umforum.ultimaker.com/index.php?/topic/1872-some-calibration-photographs/

Then modify settings like retraction distance, and print speed WHILE it is printing.

 

Share this post


Link to post
Share on other sites

Hi Guys

Sorry for not replying, I've been down with the flue.

gr5 >

1)

Retraction is ticked in Cura, and the layer view shows retraction lines.

2)

I've attached a pic. of the 'stringing'-lines. They are equivalent to the retraction lines in Cura's layer view.

They continue throughout the entire print, and are visible from the bottom layer to the top.

http://www.bredel.dk/um2/IMG_2829.jpg

3)

I have tried different retraction setting, currently running 6 mm and 30 mm/s

4)

I have tried different filaments, though all from UM and PLA

5)

I've set printing speed to 25 mm/s and travel speed to 200 mm/s

While printing, I then try to set speed to 50%, but it does not do the trick.

Temperature is around 190

Guess i'll have to try the stringing test to se if I can sort it out.

 

Share this post


Link to post
Share on other sites

So not stringing, scratching :-)

...phew there are many phenomenons and corresponding tweeks to learn.

I seem to experience many attempts where I adjust settings to avoid something and then introduce something else, or even worse, try to avoid something which appearently is me having the wrong perception of what the problem is, hence I end up wondering why none of my variations in setting makes a difference.

I love my UM2, especially when it is aided by so much expertise and guidance... one day, one day, that is me giving answers to folks!

Thanks all!

 

Share this post


Link to post
Share on other sites

Create an account or sign in to comment

You need to be a member in order to leave a comment

Create an account

Sign up for a new account in our community. It's easy!

Register a new account

Sign in

Already have an account? Sign in here.

Sign In Now
Sign in to follow this  

  • Our picks

    • Taking Advantage of DfAM
      This is a statement that’s often made about AM/3DP. I'll focus on the way DfAM can take advantage of some of the unique capabilities that AM and 3DP have to offer. I personally think that the use of AM/3DP for light-weighting is one of it’s most exciting possibilities and one that could play a key part in the sustainability of design and manufacturing in the future.