axsdenied
 Share

Recommended Posts

Posted · Printing red XT - how to improve

I finally got hold of some red Colorfabb XT, hopefully to avoid using ABS when printing some large and tough enclosures. I managed to improve the quality quite a bit but I am stuck with several problems. Any hints would be greatly appreciated.

1. Stringing:

There is leftover plastic on the sides where the head retracts and does a "jump" to the other side. See bottom of the image.

Combing was off.

Retraction was set to 40m/s, length = 4.5mm as per Colorfabb's guide here.

Travel speed was 200 mm/s which helped remove stringing a bit. I even tried 250 mm/s but it did not improve things.

Temperature 245 and 240 degrees (not much difference).

I also tried without fan and with fan at 30% (I am using dual fan mount), again I did not notice any difference.

XT is not supposed to need much fan?

I am not sure what else to try...

2. Infill

The infill looks very bad at places, big sections are missing. I don't think there was underextrusion (no stepper clicking) and the outer layers look fine. The infill was printed at the same speed as the outer layers. Fill density was 25%.

Any thoughts what happened?

Settings:

Layer height 0.2

Shell thickness 2.0 (for extra strength)

Bottom/top fills 2 (for extra strength)

Fill density 25%

Print speed 50mm/s (also tried 30mm/s for the outer shell)

Travel speed 200 and 250

Fan off and on

Temperature 240 & 245 degrees, bed at 70 degrees.

Flow 100% and 105%, it did not seem to make a difference for the infill but 100% helped a bit with the point 1.

Retraction speed 40 mm/s, length = 4.5 mm

 

IMG 20150123 124328 E

 

  • Link to post
    Share on other sites

    Posted · Printing red XT - how to improve

    Ok, here is the best I could come up with. Not much red XT left to play with :smile:

    The results are quite good. I am using simplify3D.

    • layer height: 0.2mm
    • speed: 40mm/s
    • extrusion multiplier 1.1
    • 100% fill
    • first layer speed: 66%
    • outline underspeed 50%
    • solid infill underspeed 80%
    • temperature: layer 1 = 240C, layer 2 = 245C, layer 3 = 250C.
    • glass plate at 75C (I measured the temperature of the glass plate with a thermocouple and it was roughly about 5C less than set on the printer). That 5 degrees made a huge difference.
    • fan: layer 3 10%, layer 6 30%, layer 9 40% (note that I am using https://www.youmagine.com/designs/ultimaker-2-fan-mount-dual--2 fan mount)
    • retraction: 5mm @ 40mm/s
    • x/y axis movement 250mm/s

     

  • Link to post
    Share on other sites

    Posted · Printing red XT - how to improve

    Those settings would be my advise also, except for the first layer speed.

    40mm/s is my start at 244 degrees with XT red.

     

  • Link to post
    Share on other sites

    Posted (edited) · Printing red XT - how to improve

    With my UM2,for red XT, 50% fans and no hotter than 230 to 235° & speed 40 mm/s works well.

    Edited by Guest
  • Link to post
    Share on other sites

    Create an account or sign in to comment

    You need to be a member in order to leave a comment

    Create an account

    Sign up for a new account in our community. It's easy!

    Register a new account

    Sign in

    Already have an account? Sign in here.

    Sign In Now
     Share

    • Our picks

      • New here? Get ahead with a free onboarding course
        Hi,
         
        Often getting started is the most difficult part of any process. A good start sets you up for success and saves you time and energy that could be spent elsewhere. That is why we have a onboarding course ready for
        Ultimaker S5 Pro Bundle, Ultimaker S5, Ultimaker S3 Ultimaker 2+ Connect.   
        They're ready for you on the Ultimaker Academy platform. All you need to do to gain access is to register your product to gain free access. 
        Ready? Register your product here in just 60 seconds.
          • Like
        • 11 replies
    ×
    ×
    • Create New...