Jump to content

ammar

Dormant
 View Profile  See their activity

  • Posts

    13

  • Joined

  • Last visited

    Never

 Content Type 

Posts posted by ammar

    Zusammenklebens (PLA zum PLA)!

    in Deutsch

    Posted

    Ich benutze den Roboter im Beide Wasser (Süßwasser für Test und Salzwasser für echte Mission ).

     

    Ja naturlich brache ich die Beste (Kein Problem für Preis im diesem Fall).

    Dann gehe ich zum 2-Komponenten Epoxy Spraylack. Hast du ein Link ?.

    ich habe das gefunden:

    http://www.spraymax.de/index.php?id=351

    Hast du Ahnung, wie lueft das :

     

    http://www.ottozeus.de/ottozeus/nach-anwendung/isolieren-dammen/isoliermaterialien/technicollr-8301-set.html

    Vielen Dank Voraus

     

    Zusammenklebens (PLA zum PLA)!

    in Deutsch

    Posted

    Da ich einen Unterwasser Roboter designt, würde ich die ganze PLA Körper von Roboter gegen Wasser sein.

    Ich will den Roboter für 10meter (1Bar) benutzen. Welche Material kann man benutzen um den Körber von PLA Abdichten zu sein? Genau was habe ich gemeint.

     

    Schaum und Schwämme drucken

    in Deutsch

    Posted

    Vielen Dank Nightwish. Ich habe die Filament geändert. Die graue Filament war so schlecht. Ich habe alles sauber gemacht: Feeder, Nozzle, Teflon Teil..... Aber endlich war alles wie neu wieder zurueck. Noch mal veieln Dank fuer Alles

     

    Schaum und Schwämme drucken

    in Deutsch

    Posted

    Hallo Zusammen,

     

    ich habe viele Teile so super gedruckt. Ich benutze UM2 und auf hoch Qualitat immer drucken.

     

    Seit zweit Tagen druckt mein UM2 so schlecht. Der druckt wie Schaum und Schwämme.

     

    Hat jemand so Ideen warum so druckt?

     

    Momentane Druckeinstellungen,

    Temperatur 235°C

    Bett Temperatur 60°C

    Geschwindigkeit 50mm/s

    Layerhöhe 0,06

    Infill 95%

    Das Foto sagt so besser fuer beide Drucken Vor und Nach (now)

    IMG_20141031_115434.jpg?dl=0

    https://www.dropbox.com/s/sivrgadjej8buas/IMG_20141031_115434.jpg?dl=0

     

     

     

    stick (glue) together (PLA to PLA)

    in Coffee corner

    Posted

    Hi everyone,

    I built an underwater robot. I used UM2 to create the shape. The shape of my robot like as the shape of a fish body with dimensions (65cmx25cmx15cm) and also has similar surface properties. The thickness of the outer skin of the robot approx. 3mm.

    The robot consists of several components (parts) that I was created using a 3D printer (Due to UM2 has small Dimensions).

    I used PLA filament to produce the parts of robot.

    After finishing of the printing, I got more of eight parts. (Each part has approximately the following dimensions 13cm, 18cm, 3mm).

    Of course, now comes the important aspect "stick together" (PLA to PLA)!

    I need your advice to chose the best stick of my state.

    I prefer some of the points to be the stick like:

     

    1- To be no super glue, so that the parts of the robot to remain in their position to each other over a longer period still be moved.

     

    2-The viscosity of the stick should be similar to honey and not the water.

     

    What stick would you recommend in this case for my robot?

     

     

    best regards

    Ammar

    IMG_20141023_205951.jpg

     

    Zusammenklebens (PLA zum PLA)!

    in Deutsch

    Posted

    Hallo Zusammen,

    Ich habe ein Unterwasser-Roboter gebaut. Die Form meines Roboters ähnelt die Form eines Fischkörpers mit den Maßen (65cmx25cmx15cm) und hat auch ähnliche Oberflächeneigenschaften. Die Dicke der Außenhaut des Roboters berägt fast 3mm.

    Der Roboter besteht aus mehreren Bestandteilen, die ich mithilfe eines 3D-UM2 Druckers herstellen konnte.

    Das dabei verwendete Material des Druckers ist Kunststoff, genauer gesagt PLA Filamen. Nach dem Drucken habe ich acht Teile bekommen. (Jedes Teil hat ungefähr folgende Maße 13cm,18cm,3mm ).

    Natürlich kommt nun der wichtige Aspekt des Zusammenklebens (PLA zum PLA)!

    Ich brauch Ihre Beratung bei der Auswahl eines bestimmten Klebers.

    Der Klebstoff sollte nach Möglichkeit folgende Eigenschaften in sich vereinen:

    1. Es sollte kein Sekundenkleber sein, sodass die Teile des Roboters in ihrer Position zueinander über einen längeren Zeitraum noch verschiebbar bleiben.

    2. Die Viskosität des Klebstoffs sollte der von Honig ähneln und nicht der von Wasser.

    Welches Kleben würden Sie in diesem Fall für mein 3DIMG_20141023_205951.jpg Roboter empfehlen?

    Beste Grusse

    Ammar

     

     

×
×