UltiMaker uses functional, analytical and tracking cookies. Tracking cookies enhance your experience on our website and may also collect your personal data outside of Ultimaker websites. If you agree with the use of tracking cookies, click “I agree, continue browsing”. You can withdraw your consent at any time. If you do not consent with the use of tracking cookies, click “Refuse”. You can find more information about cookies on our Privacy and Cookie Policy page.
I didn't find informations on this filament, only temperature given by the description (225-235 )C) and no heated bed, and I want to know your parameters and experience if someone already use it.
On my side, I try to print it at 30mm/sec speed and 50 mm/sec infill speed. My temperature is 230°C with a 0.4 mm nozzle and 0.15 mm layer height.
I saw underextrusion on the infill so i might slow down infill speed for the next print, setting it to 30mm/sec. A problem I have is that during extrusion can hear a sound, like sizzle, and i don't know if it's normal. Maybe the Imaterial is not dry, but i hear that sound since I start using it. Before I used sylver PLA from ultimaker and I cleaned the nozzle with the atomic method so it might not be because of dirty nozzle.
Speaking of nozzle, since I use it, there are lots of little blobs appear on the outside of the nozzle (maybe sizzle sounds is due to "projection"). Any tips for cleaning it ?
I print first a kind of sphere with the same parameters as a test piece (my goal is to print organs like liver but smaller in a first time). I put no infill and the object was very weak when I deform it. I print a cube with 20% infill to test his strenght but it is not rinsed yet.
I might post pictures later, when i will have more rinsed prints.
Please share your experience, and sorry for my very bad english :-/.
Gel-lay informations
in Materials & profiles
Posted
Hi,
I am posting here because I bought some Porolay Gel-lay http://www.formfutura.com/285mm-porolay-gellay.html and I am printing it with a UM2 extended with no modification.
I didn't find informations on this filament, only temperature given by the description (225-235 )C) and no heated bed, and I want to know your parameters and experience if someone already use it.
On my side, I try to print it at 30mm/sec speed and 50 mm/sec infill speed. My temperature is 230°C with a 0.4 mm nozzle and 0.15 mm layer height.
I saw underextrusion on the infill so i might slow down infill speed for the next print, setting it to 30mm/sec. A problem I have is that during extrusion can hear a sound, like sizzle, and i don't know if it's normal. Maybe the Imaterial is not dry, but i hear that sound since I start using it. Before I used sylver PLA from ultimaker and I cleaned the nozzle with the atomic method so it might not be because of dirty nozzle.
Speaking of nozzle, since I use it, there are lots of little blobs appear on the outside of the nozzle (maybe sizzle sounds is due to "projection"). Any tips for cleaning it ?
I print first a kind of sphere with the same parameters as a test piece (my goal is to print organs like liver but smaller in a first time). I put no infill and the object was very weak when I deform it. I print a cube with 20% infill to test his strenght but it is not rinsed yet.
I might post pictures later, when i will have more rinsed prints.
Please share your experience, and sorry for my very bad english :-/.