Hear good things about this: http://e3d-online.com/Scaffold-Support-Material
Did not try it personally (yet)
@DidierKlein could tell you more?
Edited by GuestHear good things about this: http://e3d-online.com/Scaffold-Support-Material
Did not try it personally (yet)
@DidierKlein could tell you more?
Edited by GuestI had the same issue.. I tried the PVA from ICE.. highly recommended.
It seems like ICE does not deliver to the US. I have ordered esun PVA from amazon. I will reply back with how it goes.
It seems like ICE does not deliver to the US. I have ordered esun PVA from amazon. I will reply back with how it goes.
let us know.. I have not had great experiences with esun..
I have actually cancelled my esun order because a spool of Ultimaker PVA was delivered to us last Friday. If I ever do have to go with a third party PVA, I will return to this thread.
Just thought I'd jump in about a week later and sat that the 350g spools of UM PVA are now in stock at Dynamism if anyone is interested.
Hear good things about this: http://e3d-online.com/Scaffold-Support-Material
Did not try it personally (yet)
@DidierKlein could tell you more?
Yes i tried scaffold, it's easy to print, prints nicely on the UM3.
It's not as easy to disolve as UM PVA, i have nothing fancy to dissolve i just put it in a bucket of water, for UM PVA after let's say 10 - 12h most of the support is gone, with scaffold it's not.
I have not experimented a lot with it, but i think that hot water and movement should probably decrease the waiting time.
But it's a good alternative anyway.
Recommended Posts
meduza 191
We have tried printing some with InnoSolve from Innofil3D
https://www.innofil3d.com/product/innosolve-natural-2-85mm-500gr/
It is not as good as Ultimaker PVA, it prints pretty well, but when dissolving InnoSolve it clouds the water much faster since there is some other component in it that is not transparent and dissolves slower than the pure PVA, but in a shortage of the best thing... :-)
And yes, if using PVA of any other brand, the BB core is what you should use.