I found the setting. It's a % number of the normal flow for all other layers. Mine was set at 100%, so I gingerly changed it to 95%. It seemed to slip even more. Am I right is assuming a smaller percentage should be less flow?
Yes. But you need to do about 50% to make much difference. But again, your parts wont' stick so well.
Realize that you can experiment on the fly. While it's printing the bottom layer, go into TUNE menu and set the flow to 50%. Then increase/decrease from there. It may take 10 lines drawn before the feed rate changes. If you listen to the extruder you can really hear a big difference when the flow changes as the extruder is one of the noisier steppers.
Then when you figure out the perfect value for you, you can put that into cura for future first layers.
However, this is a bad idea in the long run. Corners will lift. Parts will come loose. Bottom layers won't be as beautiful if there are gaps between the fill lines.
Recommended Posts
gr5 2,224
Initial layer flow is what you are looking for but I don't recommend you mess with it.
If you don't regulate the Z offset... it will regulate you. If you level 0.1mm higher or lower, that's a 30% difference in space. A 30% overextrusion or 30% underextrusion.
If your extruder is slipping - is it correct that you have a UM2 original (not um2+ and no feeder upgrades)? The UM2 is the one that seems to have occasional sudden slips. The fix is to do the plus upgrade or to get the meduza upgrade or the bondtech upgrade or just ignore it. I've tried all 4 of those and currently use 4 UM2s with those 4 solutions and I am happy with all 4 printers.
The problem is if you level slightly higher off the glass (or adjust initial layer flow) such that it is not slipping then you might not be squishing the filament enough and your part may come loose or the corners may curl/lift.
Link to post
Share on other sites