  1. Hi and welcome, I think the white plastic is simply red filament but very small quantities of it (as it's blocking). What kind of feeder do you have? (Ultimaker 2 or 2+?) What brand of filament? Is it old? Settings? Are you able to push filament by hand and extrude? (Like you would do for atomics)
  2. oui, c'est le paramètre qui défini la largeur de ce que tu imprime Donc pas sortie grossière de l'open world (et c'est pas près d'arriver)
  3. Then i guess you have to add some code to your stop.gcode (it's the code that is called when the printer finishes). It looks like the cr10 is now available as a printer in cura (or am i wrong?)
  4. Oui le paramètre c'est largeur de ligne ou line width en anglais
  5. Hi, What printer do you have? (You can add it to your profile) There was an issue for the um2(+) like this but i'm not sure what the status is. is it on mac?
  6. Oui bien sure l'UM2+ s'en sort pas trop mal pour l'ABS (avec porte au minimum, et capot si possible). Il faut juste un peu plus de boulot pour faire fonctionner l'ABS dessus. La m200 est vraiment bien configurée pour les matériaux Zortrax (les profils matériaux sont top) quasi rien à faire et ça s'imprime.
  7. Si tu as des questions spécifiques pour des options demande ici je ferais de mon mieux pour les expliquer (je ne les connais pas toutes mais je peux probablement faire des recherches ou aider). Sinon UM2+ ou M200(+) j'ai les deux chez moi (pas la version + de la m200 forcément). Mon avis: Si tu veux faire de l'ABS principalement (ou des dérivés filaments haut température) la m200 est quasi imbattable Si tu veux une machine plus polyvalente en matériaux, l'UM2+ est top Niveau qualité d'impression et fiabilité on est au même niveau pour moi
  8. Le bruit des gremlins c'est à cause du poulet après minuit Sinon effectivement le dépot de neige noire n'est pas inhabituel, je pense que tu peux encore tirer tes courroies un moment, sauf si tu vois que ça saute des pas de temps en temps?
  9. [Le didier du lundi] la polybox, perso je trouve qu'elle est pas adaptée pour l'um3 ou l'um2. A moins de la mettre un poil plus bas, sinon l'entrée dans le feeder se fait avec un angle assez important qui augmente fort les frottements et cause de la sous extrusion
  10. Hi and welcome to the community! I think the print speed for the grey is to high, causing that underextrusion For the green text, i think the angle is to steep and causes the print to fail, it's maybe also a problem in the model itself
  11. It would make sense to have such a service indeed. Most of the time you will only ruin the nozzle, or maybe the teflon insulator inside. Most parts could be reused to build a new core. As @tinkergnome said the core is quite difficult to take apart and put together again, it's not impossible of course but i would say you have 50% of chance to destroy it (the steel part is very fragile). Any way, if you need to change the nozzle and are willing to try it, i have some spare nozzles from creating hardcores with standard cores, so if you need one tell me
  12. Indeed there's a missing layer in that gcode. Which version of Cura is it? Anything special in your settings? This model should slice with no issues
  13. Hi and welcome, First of all be aware that new versions of the firmware have been deployed since september, maybe it's worth updating? From what i know stepper motors can reach 80°c and indeed when they heat up steps can be skipped, i'm not really aware of problems of overheating motors on the Ultimaker 3, are doing anything special? Enclosure? High Bed temperature? Ambiant temp of the room?
  14. Bonjour Jean Christophe, J'ai regardé sur le forum, je n'ai rien trouvé de semblable à priori... Tu as beaucoup de profils ou d'imprimantes enregistrées?
  15. J'arrive après la guerre mais oui toutes ces pièces sont disponibles sur mon site. Si besoin d'aide n'hésite pas à me demander par mp ou mail. Le coupleur métallique 3dsolex est plus solide que celui d'ultimaker pour info, et si tu as l'occasion prend aussi la bague métallique en remplacement du ressort c'est mieux pour la durée de vie du teflon.
  16. @darkdvd est tombé dans une marmitte d'acétone quand il etait petit (il est tout lisse maintenant) c'est pour ça qu'il ne peut plus en avoir
  17. Je ne lave quasiment jamais mes plateaux moi juste quand ca devient vraiment trop dégueu je passe à l'eau simplement
  18. Si tu veux pouvoir définir la température pour UM2 il faut changer le gcode flavour de UltiGcode à Marlin Attention il faut aussi que tu mettes un start.gcode si tu veux qu'il y ait une séquence de démarrage comme pour l'UM2
  19. Hi and welcome Can you please show a picture? And what is the model?
  20. Il faut peut être diminuer les vitesses d'impressions (le remplissage entre autre) qui pourrait causer ce genre de choses.
  21. Ca dépend de l'utilisation en effet Le TPU95A c'est pas si simple à imprimer, et c'est quand même flexible donc pas forcément adapté pour tout (par contre très solide). Le CPE perso je suis pas fan, les liaisons inter couches sont compliquées et il faut être vraiment attentif aux températures et à la ventilation. Le nylon moi j'aime beaucoup, blanc translucide ou noir chez UM effectivement assez polyvalent au niveau des utilisations Sinon tu as le ngen de Colorfabb qui existe en plusieurs coloris que je trouve pas mal et un bon compromis (entre l'ABS et le PLA) TG de 80°c et plus résistant que le PLA Ou le PLA Polymax de chez polymaker
  22. I don't know what your particular case is, but i guess that the restart or resume thing should be from the software you use to drive you printer?
  23. Si je ne dis pas de bétises le toit se fait automatiquement aussi sur des modèles non plats Et uniquement pour le toit comme dit darkdvd donc pas besoin de trop se casser la tête
×
×